Description
Silicon is considered as a promising electrode material for next-generation, high-performance lithium-ion batteries (LIBs). However, silicon undergoes huge volumetric expansion of ~400% when fully lithiated. The expansion causes massive cracking and battery capacity fade and remains one of the main obstacles to the development of advanced high-capacity LIBs. Recent studies have begun to examine the mechanistic aspect of the LIBs in search for a means to circumvent the problem of electrode cracking. In this discussion, I will discuss our recent work on investigating the fracture behaviors of silicon electrodes under various electro-chemical conditions. This study provides quantitative fracture characteristics of lithiated silicon and will aid in the development of predictive models for microstructural optimization of silicon-based LIBs.
Recommended Citation
Xia, S., & Wang, X. (2014). Fracture characteristics of lithiated silicon for lithium-ion batteries. In A. Bajaj, P. Zavattieri, M. Koslowski, & T. Siegmund (Eds.). Proceedings of the Society of Engineering Science 51st Annual Technical Meeting, October 1-3, 2014 , West Lafayette: Purdue University Libraries Scholarly Publishing Services, 2014. https://docs.lib.purdue.edu/ses2014/mms/esm/18
Fracture characteristics of lithiated silicon for lithium-ion batteries
Silicon is considered as a promising electrode material for next-generation, high-performance lithium-ion batteries (LIBs). However, silicon undergoes huge volumetric expansion of ~400% when fully lithiated. The expansion causes massive cracking and battery capacity fade and remains one of the main obstacles to the development of advanced high-capacity LIBs. Recent studies have begun to examine the mechanistic aspect of the LIBs in search for a means to circumvent the problem of electrode cracking. In this discussion, I will discuss our recent work on investigating the fracture behaviors of silicon electrodes under various electro-chemical conditions. This study provides quantitative fracture characteristics of lithiated silicon and will aid in the development of predictive models for microstructural optimization of silicon-based LIBs.