Nanophase hydroxyapatite coatings for dental and orthopedic applications

Michiko Sato, Purdue University

Abstract

In order to improve dental and orthopedic implant performance, the objective of this study was to synthesize nanocrystalline hydroxyapatite (HA) powders to coat metals (specifically, titanium and tantalum). Precipitated HA powders were either sintered in order to produce UltraCaP HA (or microcrystalline size HA) or were treated hydrothermally to produce nanocrystalline HA. Some of the UltraCaP and nanocrystalline HA powders were doped with yttrium (Y) since previous in vitro studies demonstrated that Y-doped HA in bulk improved osteoblast (or bone-forming cell) function over undoped HA. The nanocrystalline HA powders were also mixed with nanophase titania powders because previous studies demonstrated that titania/HA composite coatings increased coating adhesive strength and HA nucleation. These powders were then deposited onto titanium by a novel room-temperature process, called IonTiteT™. The results demonstrated that the chemical properties and crystallite size of the original HA powders were maintained in the coatings. More importantly, in vitro studies showed increased osteoblast (bone-forming cell) adhesion on the single phase nanocrystalline HA and nano-titania/HA coatings compared to traditionally used plasma-sprayed HA coatings and uncoated metals. Results further demonstrated greater amounts of calcium deposition by osteoblasts cultured on nanocrystalline HA coatings compared to UltraCaP coatings and conventionally used plasma-sprayed HA coatings. To elucidate mechanisms that influenced osteoblast functions on the HA coatings, the amount of proteins (fibronectin and vitronectin) onto the HA powders and the adsorbed fibronectin conformation were investigated. Exposure of cell integrin binding domains (in fibronectin III10 segments) was greater in fibronectin adsorbed onto 1.2 mole% Y-doped UltraCaP HA coatings compared to nanocrystalline HA coatings tested. However, 1.2 mole% Y-doped UltraCaP HA coatings did not increase mineralization by osteoblasts compared to the nanocrystalline HA coatings. These results suggested that the availability of integrin binding domains in fibronectin did not correlate to enhanced mineralization by osteoblasts on nanocrystalline HA coatings. Lastly, undoped nanocrystalline HA coatings were studied using a well-established rat calvaria in vivo. Histological analysis showed that nanocrystalline HA coated on tantalum scaffolds increased bone and fibrous tissue infiltration into the scaffolds while uncoated and UltraCaP HA coated scaffolds did not after as early as 6 weeks. In summary, these results encourage further studies on nanocrystalline IonTiteTM HA coatings on various metals for orthopedic and dental applications.

Degree

Ph.D.

Advisors

Slamovich, Purdue University.

Subject Area

Biomedical engineering|Materials science

Off-Campus Purdue Users:
To access this dissertation, please log in to our
proxy server
.

Share

COinS