Abstract

The colloidal microstructure of concentrated suspensions containing anionic comb- polymer-stabilized magnesium oxide (MgO) particles in water was analyzed by shear rheometry for indications of changes in particle microstructure based on particle size and comb-polymer usage. As the suspensions were sheared at different rates, jamming in the sheared MgO suspensions was observed as shear stress overshoots. The shear-induced evolution of the suspension’s microstructure was strongly related to the perceived interactions between neighboring MgO particles in the suspension. In the jammed state, interactions are believed to be enhanced by the formation of entanglements between opposing comb-polymer side-chains. Steric repulsion between side-chains was lessened for large particles on account of their diameters, which further enabled side-chain entanglement during close particle contact under shear. Suspensions with relatively wide particle size distributions (0.5 to 400 μm) were theorized to form hydrocluster aggregates, while suspensions with narrower particle size distributions (0.5 to 40 μm) most likely resulted in networked microstructures under the influence of the chain entanglements from the adsorbed comb-polymer.

Comments

This is the author's accepted manuscript version of Murray, L. and Erk, K. (2014). Jamming rheology of model cementitious suspensions composed of comb‐polymer stabilized magnesium oxide particles. J. Appl. Polym. Sci. 131, 40429, doi: 10.1002/app.40429

Keywords

solloids, rheology, structure-property relations, surfaces and interfaces

Date of this Version

1-13-2014

DOI

10.1002/app.40429

Share

COinS