Keywords
Reinforced concrete, corrosion, bond-slip, cyclic loading, performance degradation
Abstract
This paper studied the effects of reinforcement corrosion on bond performance between rebar and concrete. Tests were carried out to evaluate the degradation of bond between reinforcing steel and concrete for different corrosion levels of reinforcing steel. A series of 20 specimens of different concrete strength with various reinforcing steel corrosion levels were designed and manufactured. Each specimen was casted as a 200-mm concrete cube, and a steel rebar was centrally embedded with two stirrups around it. The steel rebar were corroded using an electrochemical accelerated corrosion technique. The corrosion crack opening width and length were recorded after the corrosion process. Then, monolithic pull-out loading tests were carried out on the specimens. The effects of reinforcement corrosion on crack opening, maximum bond stress, and energy dissipation were discussed in detail. It was found that reinforcement corrosion has non-negligible effects on bond performance of reinforcing bar in concrete.
DOI
10.5703/1288284316147
Included in
An Experimental Study on Effect of Steel Corrosion on the Bond–Slip Performance of Reinforced Concrete
This paper studied the effects of reinforcement corrosion on bond performance between rebar and concrete. Tests were carried out to evaluate the degradation of bond between reinforcing steel and concrete for different corrosion levels of reinforcing steel. A series of 20 specimens of different concrete strength with various reinforcing steel corrosion levels were designed and manufactured. Each specimen was casted as a 200-mm concrete cube, and a steel rebar was centrally embedded with two stirrups around it. The steel rebar were corroded using an electrochemical accelerated corrosion technique. The corrosion crack opening width and length were recorded after the corrosion process. Then, monolithic pull-out loading tests were carried out on the specimens. The effects of reinforcement corrosion on crack opening, maximum bond stress, and energy dissipation were discussed in detail. It was found that reinforcement corrosion has non-negligible effects on bond performance of reinforcing bar in concrete.