Characterization and evaluation of cadmium indate photocatalysts for solar hydrogen conversion
Abstract
Alternative energy sources are needed to respond to the continued increase in the global energy needs and a potential decrease in the future supplies of fossil fuels. Solar hydrogen conversion in which sunlight is harnessed to split water into H2 fuel and O2 is a promising source of energy because it is renewable and produces no CO2. A number of semiconducting oxide materials have shown promise for overall water splitting for the generation of hydrogen over the years. In this work we focus on the synthesis and analysis of undoped and C-doped cadmium indate (CdIn2O 4) thin films and nanoparticle powders, and their evaluation for hydrogen evolution via water splitting. The catalyst was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV-vis, scanning electron microscopy (SEM), and BET surface adsorption measurements. Spray and sol-gel pyrolysis methods were used for the synthesis of the materials. Doping C into CdIn 2O4 leads to enhancement in light absorption and the band gap was determined to be 2.3 eV in the nanoparticle powders. Carbon doping improves the photocurrent density by 33% and the H2 evolution rate by a factor of two. The performance of C-doped CdIn2O4 were optimized with respect to several synthetic parameters, including the In:Cd molar ratio and glucose concentration, calcination temperature, and the film thickness while the nanoparticles were additionally optimized to F127 concentration and platinum cocatalyst loading. Hydrogen generation activity was evaluated under UV-visible irradiation without the use of a sacrificial reagent and using bandpass filters the quantum efficiency was determined. Compared to platinized TiO2 in methanol C-CdIn2O4 showed a 4-fold increase in hydrogen production. The material was capable of hydrogen generation using visible light only and with good efficiency even at 510 nm. Using natural sunlight illumination, the material evolved hydrogen at a rate of 17 µmol h-1. These studies show carbon-doped cadmium indate to be a promising catalyst for solar hydrogen conversion.
Degree
Ph.D.
Advisors
Raftery, Purdue University.
Subject Area
Alternative Energy|Chemistry|Materials science
Off-Campus Purdue Users:
To access this dissertation, please log in to our
proxy server.