Sorption and photochemistry of manufactured carbon nanomaterials in the aquatic environment

Chia-Ying Chen, Purdue University

Abstract

With the growing use of carbon-based manufactured nanoparticles, including buckminsterfullerene and single-walled carbon nanotubes (SWNTs), it is likely that they will enter the environment through use, disposal, and spills; however, their environmental fate and subsequent effects on ecosystems have not been extensively studied. One of the key knowledge gaps in understanding their effects on the environment is the lack of quantitative data on their transformations in the natural environment, which is crucial for lifecycle analysis. To this end, this study has examined two potentially important environmental fate processes—sorption the photoreactivity—of these nanomaterials. Although C60 is extremely hydrophobic, molecular C60 does exist in water, and it is through this dissolved concentration or activity that its environmental distribution will be regulated (i.e., thermodynamically controlled), including its self-association to form clusters or nanoparticles. The distribution of C60 between soil and mixtures of ethanol (EOH) and water were measured at ethanol mole fractions ranging from X EOH = 1.0 to 0.4 for two soils. By measuring K p at XEOH = 1.0 for a series of soils that ranged in organic carbon and clay mineral content, possible mineral contribution to the overall partition process was found for some of the soils. After correcting for any mineral contribution to sorption, the organic carbon normalized partition coefficient, Koc, at each value of XEOH was calculated from the measured Kp values. Through a classical thermodynamic relationship, the Koc values determined at XEOH = 1.0 to 0.4 were extrapolated to estimate the pure water (i.e., XEOH = 0) Koc value of 107.1 (L/kg). Accounting for dissolved organic matter (DOM) in any natural water-soil mixtures may lower this estimate by over a factor of 2, placing this estimate in good agreement with C60’s octanol-water partition coefficient, Kow (= 106.7). Also, the photoreactivity of single-walled carbon nanotubes (SWNTs) that (i) have been functionalized via acid oxidation to contain carboxylic acid groups, (ii) further functionalized via esterification with polyethylene oxide groups, or (iii) are unmodified (i.e., unfunctionalized) was examined. Aqueous colloidal dispersions of both types of functionalized nanotubes generated reactive oxygen species (ROS) including singlet oxygen (1O 2), superoxide anion (O2·−), and hydroxyl radicals (·OH) in light within the solar spectrum (λ = 300 to 410 nm) under aerobic conditions. Defects in the fullerene surface caused by functionalization, as well as differences in amorphous carbon and metal impurity content within the different SWNT preparations, may facilitate ROS production. Experiments suggest that the metal impurities may especially contribute to ·OH generation. It appears that the functionalized nanotubes can act as the electron donors directly (resulting in a change in their properties) or can shuttle electrons from other electron donors to form these reactive oxygen species. Addition of NADH as an electron donor to colloidal dispersions of carboxylated SWNTs resulted in O2·− generation in the absence of light, suggesting dark reaction electron transfer as a potential mechanism of toxicity.

Degree

Ph.D.

Advisors

Jafvert, Purdue University.

Subject Area

Civil engineering|Environmental engineering

Off-Campus Purdue Users:
To access this dissertation, please log in to our
proxy server
.

Share

COinS